DATA SHEETS OF PHYSICAL PROPERTIES FOR SELECTED MATERIALS:

ABS/Polycarbonate Alloys..... Ask also about HIPS, GPPS, ABS, SAN

http://www.polymersales.com/contact.html

Polystyrene:                                            Ask also about HIPS, GPPS, ABS, SAN
                                                                                     http://www.polymersales.com/contact.html

Silicone Filled

Polypropylene:

Talc Filled

Calcium Carbonate Filled

Glass Fiber

Combination of fillers

Super High Impact

Polyethylene:

Calcium Carbonate Filled
Fiberglass Filled

   Purging Compound

                        Chemical Purging Compounds for All Thermoplastics Processing Machinces

Polypropylene Compounds (Calcium Carbonate Filled)

MATERIAL TYPE	CaCO3/HOMOPOLYMER				CaCO3/COPOLYMER
Part No.	P2120	P2130	P2140	P2150	P2220	P2230	P2240	P2250
Calcium Carbonate %	20	30	40	50	20	30	40	50
Density g/ml (D792)	1.05	1.15	1.25	1.35	1.05	1.15	1.25	1.35
Durometer Shore D (D2240)	71	74	77	80	69	70	72	75
Tensile Strength psi (D638M)	4400	4000	3600	3200	3500	3350	3200	3150
Tensile Mod. x100K psi (D638)	3.1	3.6	3.8	4.0	2.9	3.2	3.5	3.8
Flex Mod. x100K psi (D790M)	2.4	3.0	3.8	4.4	3.1	3.0	3.0	2.9
Flexural Strength psi (D790M)	4200	5200	6200	7200	4000	4450	4900	5350
Izod Impact Notched ft.lb./in.	0.5	0.5	0.5	0.3	1.2	1.1	1.0	0.9
Heat Distortion @
C at 66 psi	93	99	107	115	87	94	101	118
C at 264 psi	68	70	72	74	54	57	60	63
Mold Shrink in/in (D955)	.015	.014	.012	.010	.015	.014	.014	.013

All values are approximations for general design planning only. Please request specific and detail physical characteristics and attributes. You should check with the vendor before processing this material or assuming characteristics.

Combination Mineral Filler
Part No. P9230

Property	Average Value	ASTM Method
Mineral Content, %	30	N/A
Melt Flow, g/10 min.	7-12	D1238
Specific Gravity, g/cm^3	1.15	D792
Tensile Strength, psi @73 F	3,800	D638
Flexural Modulus, (Tangent) psi	320,000	D790
Izod Impact, ft-lb/in @73F Notched 1/2" x 1/8"	0.8	D256
Gardner Impact, in-lb	30	D3029
Heat Deflection, F
@264 psi	150	D648
@ 66 psi	220	D648
Hardness Shore "D"	74	D2240

All values are approximations only and are to be used for general design purposes only. Customer should request specific and detail physical characteristics from vendor. Consult with vendor before processing this material or assuming any characteristics.

Fiberglass Reinforced Polypropylene
Super High Impact
Part Numbers: P8210; P8220; P8230

Property	ASTM Method	Average Values
Fiberglass Content %		10	20	30
Melt Flow, g/10 min.	D1238	7-12	12-20	7-12
Specific Gravity, g/cm^3	D792	0.97	1.04	1.13
Tensile Strength, psi @73F	D638	5,200	6,100	6,700
Flexural Modulus, (Tangent) psi	D790	310,000	400,000	540,000
Izod Impact, ft-lb/in @73F Notched 1/2" x 1/8"	D256	4.0	4.0	4.0
Gardner Impact, in-lb	D3029	40	40	40
Heat Deflection, F
@264 psi	D648	225	0230	240
@ 66 psi	D648	245	250	260
Hardness Shore "D"	D2240	39	71	75

All values are approximations and are to be used for general esign work only. Request specific and detail physical characteristics and attributes from vendor. Consult with vendor before processing this material or assuming any characteristics.

Polypropylene Compounds
(Talc Filled)

MATERIAL TYPE	TALC/HOMOPOLYMER		TALC/COPOLYMER
Part No	P1120	P1140	P1220	P1225
TALC %	20	40	20	25
Density g/ml (D792)	1.04	1.20	1.04	1.15
Durometer Shore (D2240)	72	74	70	68
Tensile Strength psi (D638M)	4900	4100	4500	3800
Tensile Modulus x100K psi (D638)	3.3	3.4	2.8	3.3
Flexural Strength psi (D790M)	6300	6800	5700	5500
Flexural Modulus x100K (D790M)	3.3	3.8	2.8	3.4
Izod Impact Notched ft.lb/in	0.5	0.4	1.0	0.5
Heat Distortion @
Deg. C at 66 psi	117	133	116	127
Deg. C at 264 psi	73	84	63	78
Mold Shrinkage in/in (D955)	.016	.012	.014	.015

Super High Impact
(Rubber Modified - P2535)

MATERIAL PROPERTIES	METHOD	UNITS	VALUES
Mineral %			35
Density	D729	g/ml	1.20
Tensile Properties:	D638
Strength		psi	2600
Modulus		psi	145000
Elongation at Yield		%	12
Elongation at Break		%	>500
Flexural Properties:	D790
Strength		psi	3600
Modulus		psi	161000
Izod Impact Properties	D256
Notched at 23 Deg. C.		ft. lb./in.	>10
Heat Distortion @:	D648
66 psi		203 Deg. F.	95 Deg. C.
264 psi		115 Deg. F.	46 Deg. C.
Coef. of Linear Termal Expansion	D696	0.00001 in./in. Deg. F.	4.0
Impact Resistance (Falling Wt. @23 Deg. C.)	D5420	ft.lb./in.	approx. 250
Mold Shrinkage (linear)	D955	in/in.	0.017
Flammability	UL94		HB

All values are approximations for general design planning only. You should check with the vendor before processing this material or assuming any characteristics. Contact vendor for specifications.

We are known by the companies we serve.

Custom COLORS. U.V. Protection.
U.L. & Specifications Certifications

Ask Us:
Phone: 770-483-6977 Cell: 770-365-0810 Fax: 770-483-7426
E-Mail: wsmith@polymersales.com

Home About Us Contact Us